Fibra de polipropileno
1,Description:
ELT-fiber Made by 100% virgin homopolymer polypropylene multifilament (monofilament) fibers was produced by our patent advanced technology for fiber spinning, modified by adding functional additive and special surface-treating. Mixing into cement concrete, it has many advantages such as good dispersing,better water affinity, strong linking force. It is suited to reinforce and crack-resist to every kinds of cement concrete and mortar, specially used in engineering of building surface, floor, wall etc….. ELT-Fiber have five type: Micro Synthetic Fiber: monofilament and Fibrillated, Macro Synthetic Fiber: Wave,Twist/hybrid,Embossed.
ELT-Fiber for concrete reinforcement that complies with ASTM C 1116, Standard Specification for Fiber Reinforced Concrete and Shotcrete.
Micro Synthetic Fiber ELT-Mono Micro Synthetic Fiber ELT-Fibril Macro Synthetic Fiber ELT-Embossed
Macro Synthetic Fiber ELT-Twist Macro Synthetic Fiber ELT-Wave Hook End Steel Fiber ELT-HE
2,Specification:
1) Micro Synthetic Fiber ELT-Mono :
Raw Material : |
Polypropylene |
Crack Elongation: |
20+/-5% |
Fiber Type : |
Monofilament PPMF-A |
Fiber Diameter: |
18+/-2um |
Melting Point(C Deg.) : |
160 - 170 |
Density(g/cm3) : |
0.91+/-0.01 |
Acid &Alkali Resistance : |
Strong |
Tensile Strength(MPa): |
450 min. |
Length: |
Times of 4mm or 6mm |
Water absorbency : |
NO |
Normal Length |
4mm, 6mm, 8mm, 12mm,18mm, 24mm, 30mm etc...(times of 4mm or 6mm with 1mm more or less ) |
Dosage:0.5KG to 1.8KG Per CBM Concrete.
Standard Packing: 1kg/PE Film bag,20kg/Plastic Woven bag,9500KG/20'gp without Pallets,Other packing can as per your request.
2)Micro Synthetic Fiber ELT-Fibril
Density(g/cm3) |
0.91 |
Elastic Modulas (MPa) |
>3500 |
Length(mm) |
Times of 4mm or 6mm |
Equivalent Diameter um |
100 +/- 50 |
Shape |
Beam-like Net |
Crack Elongation(%) |
20+/-5 |
Acid &Alkali Resistance |
Strong |
Water-Absorbency |
No |
Tensile Strength(MPa) |
>450 |
Melting Point(ºC) |
160 --170 |
Normal Length: |
6mm,8mm,12mm,18mm,24mm,30mm etc..(times of 4mm or 6mm with 1mm more or less ) |
Dosage:0.5KG to 1.8KG Per CBM Concrete.
Standard Packing: 1kg/PE Film bag,12kg/Plastic Woven bag,6000KG/20'gp without Pallets,Other packing can as per your request.
3)Macro Synthetic Fiber ELT-Embossed
Raw Material |
Virgin grade polypropylene |
Tensile Strength(MPa): |
550 min. |
Water Absorbency: |
No |
Density(g/cm3) : |
0.91+/-0.01 |
Melting Point(C Deg.) |
160 - 170 |
Elastic Modulas(Mpa): |
9000 min |
Acid & Alkali Resistance |
Excellent |
Equivalent Diameter |
0.8mm |
Moisture Content |
0.0% |
Fiber Type |
Embossed |
Color |
White, Black, Gray,Natural |
Length: |
30mm,48mm, 55mm, 60mm,65mm or as per request |
Tandard Dosage |
2kg/m3 to 6kg/m3 |
Standard Packing: 5kg/Carton Box,1200KGS/Pallets,12000KG/20'gp
4)Macro Synthetic Fiber ELT-Twist
Density(g/cm 3 ) |
0.91 +/- 0.01 |
Equivalent Dia(mm) |
0.3±0.05 |
Shape |
twist |
break tensile Ratio(%) |
8-15 |
Crack Ratio (%) |
20+/-5 |
Melting point ( C. Deg) |
160-170 |
Tensile Strength (Mpa) |
500 to 800 |
Water Absorption |
Negligible |
Elastic Modulus (Mpa) |
>3500 |
Resistance to acid & alkali |
Excellent |
Material |
Virgin Copolymer/Polypropylene |
Length(mm) |
38/48 /54 or as per your request |
Dosage rates will vary depending upon the reinforcing requirements and can range from 2kg/m³ to 5 kg/m³ |
Standard Packing: 1kg/PE Film bag,10kg/Plastic Woven bag,5000KG/20'gp without Pallets,Other packing can as per your request.
5)Macro Synthetic Fiber ELT-Wave
Raw Material |
100% virgin polymer |
Tensile Strength(MPa): |
500 min. |
Water Absorbency: |
No |
Density(g/cm3) : |
0.91+/-0.01 |
Melting Point(C Deg.) |
160 - 170 |
Elastic Modulas(Mpa): |
5000 min |
Acid & Alkali Resistance |
Excellent |
Equivalent Diameter(mm) |
0.8-1.2 |
Moisture Content |
0.0% |
Fiber Type |
Wave/Curved |
Color |
White, Black |
Crack Elongation(%) |
15+/-5 |
Length: |
30mm,48mm,54mm, or as per request |
Dosage |
2kg/m3 to 3kg/m3 |
Standard Packing: 1kg/PE Film bag,10kg/Plastic Woven bag,3000KG/20'gp without Pallets,Other packing can as per your request.
3, Applying Instruction:
1), Matching Ratio:
Usually, it is no need to Change the matching ratio of the concrete. Considering the requirement of fissure-resistant, the polymer fiber is
recommend to combine withThe polypropylene fiber mesh with the volume ratio of 1: 1 ( 0.9kg fiber-mesh per sqm Of cement concrete).
2), Mixer Adoption: Double-axle horizontal compelling mixer is priority.
3), Mixing process:
Crushed stones, fibers and sands are put into the mixer in succession. After stirring for two minutes, fiber will fully spread and then add cement
and water and stir normally. The addition of materials also can be put into as common concrete, but the stirring time should be properly prolonged
to make fiber completely Mixed.
4), Shaping & Maintenance
There is no special requirement, may along the vibrating time for 30s, The maintenance of the fibre concrete should be done same as
the normal concrete.
5), Economy:
Compared with steel fiber, Polymer fibre has the advantages of corrosion and wear-resistant reducing 50% cost with same volume to steel fibre.
4, Our Company Information:
Anhui Elite Industrial Co.,LTD was established in 2007, has become one of the leading and professional suppliers of all kinds of Concrete
Reinforcement Fibers in the world market. Our Product were widely used in all kinds of concrete,mortar,plaster projects and exported to
more than 30 countries, Such as USA, Russia, Germany, Australia, Chile, UAE, Korea, Vietnam, Africa etc.
Our Fibers was made by 100% Virgin Material with advanced equipment of yard and cutting, we have one full set of precise testing instrument,
testing equipment and quality inspection team, technology research and development team. the management system was certified by ISO9001
and our products have been passed the CE Certification.
Our Mainly Product and Production Capacity as below:
Item |
Capacity/Annual |
Polypropylene Fiber (PP Fiber) |
15000mts |
Polyester Fiber(PET Fiber) |
6000mts |
Polyvinyl Alcohol Fiber( PVA Fiber) |
30000mts |
Polyacrylonitrile Fiber(PAN Fiber) |
6000mts |
Naphthalene Formaldehyde Sulphonate |
300000mts |
Polycarboxylate Superplasticizer |
150000mts |
5,Our Certificate: