Homopolymer Multifilament Polypropylene Microfiber Fiber

• Customization: Available
• Application: Concrete Reinforcement, Cement, Concrete, Mortar
• Color: White, White
• Model NO.: ELT-PPFM
• Length: 4mm to 65mm, Times of 4mm/6mm with 1mm More or Less
• Material: Polypropylene, 100% Polypropylene
• Tenacity: High Tenacity
• Type: Microfiber
• Fiber Type: Monofilament
• Raw Material: 100% Virgin PP
• Crack Elongation: 20+/-5%
• Fiber Diameter: 20-30um
• Tensile Strength(MPa): 450 Min.
• Acid & Alkair Resistance: Strong
• Melting Point(C Deg. ): 160-170
• Certificate: ISO and CE
• Density: 0.91+/-0.01um
• Usage: Concrete
• Pattern: Plain
• Feature: Anti-Cracking
• Function: Reinforce The Concrete
• Structure: Monofilament
• Transport Package: 18kgs 20kgs Per Bag
• Specification: 0.6/0.9/1.0kg per PE bag or paper bag
• Trademark: ELITE-INDUS
• Origin: Anhui
• HS Code: 55034000
• Production Capacity: 600mts/Month
• Package Size: 80.00cm * 55.00cm * 25.00cm
• Package Gross Weight: 21.000kg

Product Description

 multifilament Polypropylene Microfiber fiber

EltFiber-PPMF Polypropylene microfiber was produced by referring foreign advanced technology for fiber spinning, modified by adding functional additive and special surface-treating.
Mixing into cement concrete, Polypropylene microfiber has many advantages such as good dispersing, better water affinity, strong linking force.

Polypropylene microfiber is suited to reinforce and crack-resist to every kinds of cement concrete and mortar,
specially used in engineering of building surface, floor, wall etc…

1, Our Polypropylene microfiber are made by 100% Virgin Polypropylene material
2, We make the pp yarn by ourselves. We always have stock and make delivery in 3-7 days
3, Capacity 1500Ton/Month, 18000Ton/Year Production


Brief specification of Polypropylene microfiber
Compliance:  ASTM C1116, Type III   BS EN 14889 - 2

1, Normal Type MicroFiber Monofilament PPMF-A

Raw Material	Polypropylene	Crack Elongation	20+/-5%
Fiber Type	Monofilament PPMF-A	Fiber Diameter	20-30um
Melting Point( C Deg.)	160 - 170	Density (g/cm3)	0.91+/-0.01
Acid & Alkali Resistance	Strong	Tensile Strength (MPa)	450 min.
Length	Times of 4mm or 6mm	Water absorbency	NO
Normal Length	4mm, 6mm, 8mm, 12mm,18mm, 24mm, 30mm etc... (times of 4mm or 6mm with 1mm more or less )

 
2. Special Type pp MicroFiber Monofilament
A. pp MicroFiber Monofilament PPMF-B:High Tensile Strength -----------600MPa Min
B. pp MicroFiber Monofilament PPMF-C:Superfine-------------------------20+/-2um Dia

Packing of Polypropylene microfiber

PP Fiber Shape	Inner Packing (PE film bag)	Outer Packing (Plastic Woven bag)	20'gp	40'HQ
Monofilament	0.6/0.9/1.0 kg	18/20kg	11000kg	23000kg
	Inner Packing  (water Soluble paper bag)	Outer Packing  (Carton)
Monofilament	0.6/0.9/1.0 kg	18/20kg	8000kg	18000kg

 
Functions: 
• Resist to shrink & crack            
• Increase seepage resistance
• Increase friction resistance          
• Increase freezing & thawing resistance                              
• Improve tendons protection         
• Replace steel net (using in plastering)
• Prevent mortar split and crackle expansion  
• Increase impact resistance and peeling resistance

Advantages
• Cost effective
• Replaces anti crack mesh reinforcement
• Decreases construction time and labor
• Inhibits intrinsic cracking in concrete           
• Disperses uniformly throughout the mix
• Do not rust
• Explosive spall control

Applications:
A). suit for the waterproof layer, floor, inner & outer wall of industrial and civil construction.
B). Increase cracking resistance on the surface of industrial workshop, warehouse and parking lot.
C). Increase cracking & seepage resistance of the ground in natatorium, swimming pool, pond and ditch.
D). Suit for any mortar projects and common concrete projects.
E). Highway, bridge and other roads.

Applying Instruction:
A). Dosage:  for resist the common cracks on surfaces, 0.9kg/m3 fibers to cement mortarIs enough, and for increasing reinforce and seepage resist application 1.8kg/m3 is enough.
B). Stirring requirement: The proportion of cement, sand and aggregate is no need to be changed. Put cement, aggregate, additive and fiber together, then stir after adding enough water and time for stirring can be prolonged for 2~3 minutes in order to make the compound mix completely. Also it can be mixed with cement and other aggregates in advance, stirring by adding water at worksite before construction.

Our Company:

ELITE was established in 2007, has become one of the leading and professional suppliers of many kinds of Concrete Reinforcement Fibers in the world market.

ELITE fibers are made by 100% virgin materials with advanced equipment of yarn and cutting. We have one full set of  precise testing instrument and quality inspection team, technology research & Development team.

Elite own a team with 10+ years experience.We know well of Chinese Concrete reinforcement fibers   on technical inspection, marketing, transportation.

Pls feel free to contact us freely at any time