Polypropylene PP Fiber Monofilament Fibre

• Customization: Available
• Color: White
• Type: Concrete Fiber
• Model NO.: Elt-PPMF
• Length: 4, 6, 8, 12, 16, 18, 20, 24, 28, 30mm, Times of 4mm or 6mm
• Crack Elongation: 20+/-5%
• Fiber Diameter: 20um-30um
• Density(g/cm3): 0.91+/-0.01
• Product Name: PP Fiber Grade PP Monofilament Fibre
• Raw Material: 100% Vigin Polypropylene
• Fiber Type: Monofilament
• Acid &Alkali Resistance: Strong
• Tensile Strength(MPa): 450 Min.
• Transport Package: 0.6kg or 0.9kg a PE Bag, 18kg/ Plastic Woven Bag
• Specification: CE
• Trademark: elite-indus
• Origin: Anhui
• HS Code: 5503400000
• Production Capacity: 1000tons Per Month
• Package Size: 100.00cm * 55.00cm * 25.00cm
• Package Gross Weight: 22.000kg

Product Description

PP Fiber Grade PP Monofilament Fibre

                                                                                                  EltFiber-PPMN

1, PP Monofilament Fibre Description:
EltFiber-PPMN PP monofilament fiber was produced by referring foreign advanced technology for fiber spinning, modified by adding functional additive and special surface-treating. Mixing into cement concrete, it has many advantages such as good dispersing, better water affinity, strong linking force. It is suited to reinforce and crack-resist to every kinds of cement concrete and mortar, specially used in engineering of building surface, floor, wall etc.



2, PP Monofilament Fibre Specification

Raw Material	Polypropylene	Crack Elongation	20+/-5%
Fiber Type	monofilament	Fiber Diameter	20um-30um
Melting Point (C Deg.)	160 - 170	Density (g/cm3)	0.91+/-0.01
Acid & Alkali Resistance	Strong	Tensile Strength (MPa)	450 min.
Length	4,6,8,10, 12, 16,18,20etc. times of 4 or 6mm	water absorbency	NO

PP Monofilament Fibre Features:
A). No agglomeration and easily spread around in mortar or concrete. Guarantee the property of crack resistance effectively
B). Apply conveniently. No need to change the proportion of mortar, and just put the fibers into the mortar mixture and stir for a moment after adding water.
C). Has fine economic property. The equivalent dia. of polypropylene monofilament is only φ 0.02mm, so the ratio of dia. And surface is high and on the basis of crack resistance, it can reduce the amount (0.6kg/m 3 ) and cut down the cost effectively.
D). Be better to plaster. Because a great number of thin fibers spread into mortar evenly, so the plastering is much easier and this can improve the binding strength between surface and base.
E). The fiber has stable chemical property, strong acid &alkali resistance, and can be used in any engineering projects.

3, PP Monofilament Fibre packing:
A, 600g or 900g or 1000g / pe film bag, 18kg/ Plastic woven bag,8tons/1x20`gp,20tons/40"HQ
B, 600g or 900g or 1000g / pe film bag,18kgs/carton,7.2tons/1x20`gp
C, Water soluble bag is available also.
4,  PP Fiber Monofilament Applications:
A). suit for the waterproof layer, floor, inner & outer wall of industrial and civil construction.
B). Increase cracking resistance on the surface of industrial workshop, warehouse and parking lot.
C). Increase cracking & seepage resistance of the ground in natatorium, swimming pool, pond and ditch.
D). Suit for any mortar projects and common concrete projects.
E). Highway, bridge and other roads.

5, Typical physical properties:
(1 )PP Monofilament Fibre Functions:
A. Resist to shrink & crack
B. Increase seepage resistance
C. Increase friction resistance
D. Increase freezing & thawing resistance
E. Improve tendons protection
F. Replace steel net (using in plastering)
G. Prevent mortar split and crackle expansion H.Increase impact resistance and peeling resistance

6, PP Monofilament Fibre Applying Instruction:
A). Dosage: for resist the common cracks on surfaces, 0.9kg/m3 fibers to cement mortar Is enough,
       and for increasing reinforce and seepage resist application 1.8kg/m3 is enough.
B). Stirring requirement: The proportion of cement, sand and aggregate is no need to be changed. Put cement, aggregate, additive and fiber together, then stir after adding enough water and time for stirring can be prolonged for 2~3 minutes in order to make the compound mix completely.
Also it can be mixed with cement and other aggregates in advance, stirring by adding water at worksite before construction.

Our Mainly Fiber:


Our Company:
Re-founded in 2007, Anhui Elite Industrial Co.,Ltd (hereafter called AEI) is a professional supplier of Reinfocing Fiber including 
Polypropylene Fiber (Monofilament, Mesh, Twisted, Hybrid, Waved), Polyvinyl alcohol fiber, Polyester Fiber, Polyacrylonitrile fiber, Glass Fiber,etc....
Anhui Elite technology in China is a market leader in the design and manufacturer of innovative Concrete Fiber.
Own a team with more than 10years Concrete field working experience, on technical, inspection, marketing, transportation and after-sale service.




                 Our Advantage                                                                                    Our Service

1. We are SGS verified Chinese supplier                                     1. Free sample available 
2. CE certificate offered for some products                             2.Trial order acceptable
3. Professional Reinforcing Fiber suppliers                             3.Customized packing acceptable
4, Standard service to your orders                                               4.Flexible payment terms 
5. Small order / OEM order acceptable                                       5.Certified cargo inspection process